Dawang Steel Casting Foundry
Dandong Dawang Steel Castings is a leading manufacturer of high-precision and high-complexity steel casting products and machined components for diverse industries based in China. With decades of steel casting experience, we work to best serve our clients.
steel casting foundry services
Investment Casting, Sand Casting, Machining
Our steel casting foundry services include stainless steel casting, alloy steel casting, carbon steel casting, manganese steel casting, and the manufacturing of other metal casting products. Casting products of our steel casting foundry span across many industries, including but not limited to agriculture, automotive and railroad, petrochemical, and constructional industry.
PROUD of Dawang steel casting foundry
Building The Future of steel casting industry
In 2018, Dawang Steel Castings celebrated its 20 year anniversary. Since our founding, we have built a rich tradition of excellence. We’re the premier steel investment casting foundry in China and highly regarded across the steel casting industry.
Watch the video of dawang steel casting foundry to learn more about our successful journey and future goals!
Dawang served clients across three continents— Asia, North America, and Europe. Our major clients are from USA, Canada, Japan, Germany, Italy, France, Australia, UK, etc.
We have built and maintained a close relationship with our clients for the past 20 years by providing them with the best customer service and steel casting products.
FAQ about our Steel Casting Foundry
If your questions are not answered below, feel free to contact Dawang Steel Castings today!
DAWANG, as one of the outstanding steel casting manufacturers and the leader steel casting company in China, provides excellent casting products for their customers. Our steel casting foundry achieves:
Investment casting/lost wax casting, sand casting, and shell mold casting.
As a professional steel casting company, we have 3 steel casting foundries and provide specialized parts casting services like housing casting, and cast different materials like low carbon steel casting. With our steel casting foundry, you will achieve a flexible combination of parts, materials, and casting methods. For example, housing stainless steel investment casting.
Compared with other steel casting manufacturers, we are trying to produce “Best Metal Casting China” and improve our steel casting company to be better. We are working for the result that no matter you want to create housing casting, low carbon steel casting, or stainless steel investment casting, once you searched “Metal Casting China”, you will find our steel casting company.
Casting capacity depends on the performance of steel casting manufacturers and the number of steel casting foundry the company has. Any excellent steel casting company usually has more than one steel casting foundry, and the more steel casting foundry it has, the more casting capacity it has.
As one of the famous steel casting manufacturers, we have 3 steel casting foundries in China, and our current annual capacity is 18,000 tons.
The range of weights and sizes for the casting products depends on the casting capacity of steel casting manufacturers.
As the leader of the steel casting company in China, we are capable of producing a variety of casting products across different industries and applications. Our casting statistics is as the following:
Weight: 0.1 – 1500 kg
Size: 1800*2500*1000 mm
Besides, we have more than one steel casting foundries in China, which satisfy different product specification of our customers.
Our steel casting foundries in China provide outstanding casting service for various kinds of steel:
Carbon steel, stainless steel, alloy steel, etc.
Steel casting manufacturers that can deal with different kinds of materials, such as stainless steel, and alloy steel, are typically more flexible with clients’ needs.
Yes, as a rich experience steel casting company, we provide valve body casting service and we have our own machining workshop and provide casting parts machining service. We have our own horizontal and vertical machining center, CNC lathe, boring machine, drilling machine, and other machines.
We are the leader of steel casting manufacturers and our valve body casting service exists investment casint, sand casting, and shell mold casting. Our experienced steel casting foundry provides high quality steel casting and produces metal parts for a variety of industries. Especially, our casting parts in automobiles are durable.
We have more than one steel casting foundry and high casting capacity of valve body products. As professional steel casting company, our steel casting foundry provides advanced casting prats, safety product delivery, and satisfied after-service.
1 hole defect
Hole defects include porosity, shrinkage, shrinkage, slag hole, sand hole, iron bean.
Porosity: the charge should be cleaned, the ferroalloy should be baked well, the ladle should be baked well during pouring; the overheating temperature and time of molten metal should be controlled by reasonable melting process, the cooling rate of castings should be accelerated, or solidified under pressure, and the gas should be precipitated; the appropriate pouring process, gating system and pouring conditions should be selected to facilitate the discharge of gas; the air permeability of the mold shell should be improved, and the exhaust hole should be added when necessary; the suitable temperature of molten metal, pouring temperature and baking temperature of the mold shell should be added; the roasting mold shell should be fully roasted; the particle size of binder and refractory should be reasonably selected.
Shrinkage: correct design of gating system to facilitate casting and sequential solidification and shrinkage; improvement of casting structure to make wall thickness as uniform as possible or increase process subsidy and cold iron; use of appropriate pouring process, such as high temperature, low temperature pouring; increase mold cooling rate, or reasonable mold formation, increase wax mold spacing and improve local heat dissipation conditions; reduce molten metal temperature during pouring and increase the height of pressure head; select smelting alloy with low shrinkage if necessary.
Shrinkage: adjust alloy composition, reduce alloy solidification range, fully deoxidize and degassing during melting and pouring to reduce the effect of gas on solidification shrinkage; improve casting structure, set pouring system reasonably, increase pressure head height and increase shrinkage capacity; select suitable pouring process, strictly control pouring temperature of molten metal; select good thermal conductivity shell material, improve cooling condition of castings and speed up cooling rate of castings; improve the position of inner gate, which is beneficial to sequential solidification.
Sand hole: keep wax and gate rod clean, prevent mold shell from falling into cavity during dewaxing, handling, storage, roasting, pouring or sand filling. Before pouring, vacuum cleaner should be used to clean the mold cavity; select suitable shell material, reasonable shell making process, strictly operate, avoid shell layer stratification; improve gating system design, avoid direct entry of refractory material into cavity and slow down the impact of molten metal on cavity surface; pay attention to pouring operation, slow down and fast before pouring, avoid severe scour of molten metal to cavity
Slag hole: strengthen charge management, adopt clean charge when smelting; use proper amount of slagging agent and deoxidizer when smelting, molten metal should have enough static time, which is beneficial to slag floating; remove slag on ladle before pouring; improve gating system design; Improve the height of ladle nozzle to shell gate cup.
Iron beans: when coating the first two layers, pay attention to the operation, to eliminate the sharp angle, corner bubble; the new coating should be static for a certain time, when adding wetting agent, should add appropriate amount of defoamer; wax mold should be degreased before coating; improve casting design, sharp angle, corner should be smooth transition.
2 schizoid defects
Cracks include: hot crack, cold crack.
Hot crack: improve casting structure, wall thickness as uniform as possible, increase casting round corner or add process bar; improve shell material or reduce shell layer number, add appropriate amount of additive, increase pouring temperature, increase shell concession; improve pouring system design; select reasonable pouring process; select materials with low thermal cracking tendency, keep furnace clean, select reasonable smelting process, add rare earth elements in appropriate amount, improve high temperature strength and plasticity of castings.
Cold crack: improve casting structure, such as uniform wall thickness, eliminate sharp angle, add process reinforcement, control cooling rate to adapt to alloy shrinkage; adopt less phosphorus furnace, adopt reasonable melting process, reduce impurity content, improve molten metal quality; When cleaning castings or removing gate, the impact force should not be too large.
3 Surface Defects of casting products
Surface defects include sand sticking, scarring, sand clamping and cold insulation.
Sanding: reasonable selection of shell materials and ensure their quality, full deoxidation, minimization of molten metal oxidation, and removal of oxide produced; control of humidity and storage time of shell storage site, use of reasonable roasting process; proper reduction of molten metal temperature and shell temperature during pouring; improvement of casting structure and heat dissipation parts; proper improvement of surface coating viscosity; proper reduction of molten metal temperature during pouring; proper reduction of pouring temperature of molded shell; proper reduction of height of pressure head.
Scarring: the coating should be fully stirred, after hanging, the air is dry well and hardened fully; reduce the density of binder in the surface coating; reduce the temperature of molten metal and shell when pouring properly, Reduce oxide in molten metal and low melting point inclusions in shell surface; improve casting structure.
Sand clamping: prevent mold shell delamination, select reasonable pouring process, reduce stress, avoid inner surface rupture of mold shell, improve casting structure, avoid large plane or concave as far as possible, design inner gate correctly, avoid local overheating; Select reasonable shell making process and strictly implement, fully harden or dry well, make coating close combination, improve shell strength.
Cold insulation: properly increase the temperature of molten metal and shell during pouring, improve the design of gating system, increase the number and position of cross section and inner gate of gating system, so as to shorten the filling time of molten metal in cavity; properly increase pouring speed, make molten metal enter cavity continuously and smoothly, and avoid the phenomenon of breaking flow; when pouring, put cover agent in the ladle in advance to prevent secondary oxidation of molten metal; make molten metal filling smoothly during pouring.
4 Defects in size, shape and weight
Dimensional shape and weight of unqualified defects include: flying wings, inadequate pouring, deformation, dislocation, Residues in the cavity, Pit, Inclusions.
Fly wing: strictly control the temperature and waxing pressure of wax material when making mould; check the parting surface carefully and clean up before making mould; improve the design of pressing type and select material reasonably; control the manufacturing quality of pressing type, Ensure the accuracy and roughness of parting surface; specify reasonable service life.
Insufficient pouring: strictly control the temperature of wax material after stirring; strictly control the injection pressure, and contact wax injection can not be interrupted; improve the pressure design to facilitate exhaust.
Deformation: reasonable selection of binders and refractories as well as paint, shell making and pouring process; control of coating ratio, viscosity and temperature, pay attention to shell coating and hanging operation; shell to prevent a certain time to dewaxing; choose a reasonable roasting process, strictly control roasting temperature and time; strengthen the regular detection and daily maintenance of roaster; shell roasting, immediately after pouring.
Dislocation: lock the live block when pressing, counteract the pressure of wax filling; determine the reasonable service life of the pressing type; select the injection pressure reasonably according to the size, shape and wax material of the wax mold.
Residues in the cavity: After the shell is hardened, it should be fully dried; select a reasonable roasting process and strictly control the roasting temperature and holding time: regularly check the roasting furnace to meet the process requirements; thoroughly clean the sprue cup before dewaxing Excess shell material on the top to avoid the shell material falling into the cavity during the dewaxing process; select a reasonable dewaxing process to strictly control the temperature and time of dewaxing; when replacing the dewaxing solution, completely remove the dewaxing The shell material at the bottom of the tank; the shell storage place should be managed in accordance with the 5s requirements, the shell should be stored upside down to prevent the shell material from falling into the cavity; be careful to avoid sprinkling the molding sand into the cavity without pouring.
Pit: Choose dry and clean charge, choose reasonable smelting process, and adopt secondary deoxidation; choose surface layer shell material reasonably; choose reasonable shell roasting process, strictly control roasting temperature and time, and eliminate residue in the cavity Make the shell white after firing; select a reasonable binder according to the material of the casting, such as silica sol binder; appropriately reduce the temperature of the molten metal and the shell during casting to speed up the cooling rate.
Inclusions: Choose clean charge, sandblasting or shot blasting before use. Before using the alloy, it should be inspected and properly baked, and desulfurization treatment should be used if necessary; choose a reasonable melting process and pouring process, and use high temperature Use a filter screen or inert gas if necessary; deoxidize strictly during smelting to protect the surface of the molten metal. Before the molten metal is released, let it stand for 2 minutes to float the inclusions and remove them; put it in the ladle first Covering agent to prevent secondary oxidation when molten metal is poured; appropriately increase the temperature of molten metal and mold shell, which is beneficial to the floating of inclusions.
These kinds of defect are common for steel casting manufacturers. A responsible steel casting company should demonstrate those defects and provide prevent solution for their customers. As the leader steel casting company in China, we are experienced to deal with these defects and provide prefect casting products to our customers. Our steel casting foundry is capacity to satisfy your requirement.
As one of the steel casting manufacturers, we perform production in strict accordance with each technical requirement in the PPAP document.
The contents of PPAP files include: PFD, PFMEA, Control plan, Bubble Drawing, Dim Report, Material Inspected Report, Surface Inspected Report, Xray Inspection Report, MPI Report, etc.
Every steel casting foundry always obeys the quality control system. We still follow the standard of the best steel casting company in China. An we support customers visting to our casting foundry. As a responsible steel casting company, we will answer and queston about the castings.
If you want to develop new casting products, finding experienced steel casting manufacturers is important. Creating a cooperation with a professional steel casting company will save your time and costs during the product development and production process.
Dawang Steel Castings, founded in 1998, is an experienced steel casting company. We have 3 steel casting foundries in China to provide excellent, high quality steel casting. Our process is as the following:
- Send us the drawing, the content of the drawing includes weight, material, tolerance requirements, mechanical performance requirements, surface treatment requirements, heat treatment requirements and other technical parameters, preferably with 3D drawings.
- About 3-5 days to make a quotation and send it to the customer.
- After the customer finally agrees with the price, pay 50% of the mold fee in advance, and then we start to make molds and samples. The sample production cycle is about 8 weeks.
- The sample is sent to the customer. After the test is qualified, the customer pays the remaining 50% of the balance and the sample fee. The sample development process is completed.
Compared with other steel casting manufacturers, we always work closely with our customers to fulfill their needs. Our steel casting foundry provides high quality casting and safety storage service. And as a responsible steel casting company, we are quick to answer any question that you may have during the casting process.
Steel casting knowledge center & news
Learn more about the steel casting process and latest information